An In Situ High Temperature Investigation of Cation Environments in Aluminate and Silicate Glasses and Liquids at the LUCIA Beamline
Abstract
The structure of crystals and melts were obtained at high temperature using X-ray absorption at the Ca K-edge on CaMgSi2O6 (diopside), CaAl2Si2O8 (anorthite), Ca3Al2O6 (C3A) and CaAl2O4 (CA) compositions. Important changes are observed above the liquidus temperature particularly for the C3A composition where all oscillations in the XANES spectra disappear. Important changes in the Ca K-edge XANES are also visible in the pre-edge region, with increasing temperature, for crystalline CaMgSi2O6.